Product name: PBAT
Chemical name: 1, 4-Benzenedicarboxylic acid, 1, 4-dimethyl ester, polymer with 1, 4-butanediol and hexanedioic acid
CAS No.: 55231-08-8
Description
PBAT is our biodegradable, statistical, aliphatic-aromatic copolyester based on the monomers 1, 4-butanediol, adipic acid and terephthalic acid for film extrusion. It has similar properties to LDPE.
● Transparent to translucent, semi-crystalline structure with DSC melting point in the range of PE-LD: 110 –120 °C
● High ultimate elongation at break and high failure energy (dart drop)
● High, but controllable water vapour transmission rate (WVTR)
● MVR (190 °C, 2,16 kg): 2,5 – 4,5 ml/10 min.
● Good thermostability up to230 °C
● regular predrying of pellets
● Good processability on blown film lines
● Down gaging to 10 μm possible
● Weldable and printable
Specification
|
Item |
Unit |
Specification |
|
Appearance |
|
Oyster white or pale yellow granule |
|
Density |
(20℃),g/cm3 |
1.18～1.28 |
|
Melting Point≥ |
℃，(10℃/min) |
110～120 |
|
Melt Index |
G/10min,(150℃，2.16kg) |
≤5 |
|
Tensile Strength ≥ |
Mpa, (50mm/min) |
15 |
|
Elongation at Break≥ |
%，(50mm/min) |
500 |
|
Bending Strength ≥ |
MPa，(2mm/min) |
4 |
|
Flexural Modulus≥ |
MPa，(2mm/min) |
80 |
|
Notched Impact Strength≥ |
KJ/m2 |
N.B |
|
HDT≥ |
℃,(120℃/min) |
40 |
|
Loss on Drying≤ |
% |
0.3 |
|
Ash≤ |
% |
0.1 |
|
Shore D Hardness ≥ |
Hardness |
33 |